金黄色（黄色）玻璃
.........................................................................................................................................................................................................................................................
|
|
|
|
牌 号
|
厚度
(mm)
|
A[2856k]
|
D65
|
化学稳定性
|
ND
|
α×10-7
(/℃)
|
Tg
(℃)
|
Ts
(℃)
|
S
|
|
x
|
y
|
Y
|
x
|
y
|
Y
|
DA
|
DW
|
|
JB400
|
2
|
0.450
|
0.410
|
96.3
|
0.316
|
0.336
|
94.2
|
1
|
1
|
1.632
|
95
|
497
|
555
|
3.65
|
|
JB420
|
2
|
0.455
|
0.414
|
93.1
|
0.323
|
0.346
|
90.8
|
2
|
3
|
1.632
|
95
|
497
|
555
|
3.69
|
|
JB450
|
2
|
0.492
|
0.461
|
94.7
|
0.401
|
0.488
|
90.7
|
1
|
3
|
1.523
|
103
|
527
|
605
|
2.64
|
|
| |
|
| 金黄色（黄色）玻璃技术要求 |
金黄色（黄色）玻璃气泡、条纹、应力类级别 |
|
牌 号
|
厚 度(mm)
|
λtj
(nm)
|
λ0
(nm)
|
Tλ0
(%)
|
K
|
|
JB400
|
2
|
400±10
|
560
|
≥86.0
|
≥0.6
|
|
JB420
|
2
|
420±10
|
560
|
≥86.0
|
≥0.6
|
|
JB450
|
2
|
450±10
|
560
|
≥89.5
|
≥0.6
|
|
|
牌 号
|
气 泡
|
条 纹
|
应 力
|
|
JB400
|
C-B
|
3C
|
3
|
|
JB420
|
C-B
|
3C
|
3
|
|
JB450
|
C-B
|
3C
|
3
|
|
| |
|
|
|
| |
| |
|
|
|
|
牌 号
|
厚度
(mm)
|
A[2856k]
|
D65
|
化学稳定性
|
ND
|
α×10-7
(/℃)
|
Tg
(℃)
|
Ts
(℃)
|
S
|
|
x
|
y
|
Y
|
x
|
y
|
Y
|
DA
|
DW
|
|
JB470
|
2
|
0.492
|
0.462
|
96.0
|
0.401
|
0.490
|
92.0
|
1
|
3
|
1.523
|
103
|
527
|
605
|
2.64
|
|
JB490
|
2
|
0.502
|
0.468
|
94.5
|
0.422
|
0.514
|
89.6
|
1
|
3
|
1.523
|
103
|
527
|
605
|
2.64
|
|
JB510
|
2
|
0.519
|
0.471
|
91.5
|
0.456
|
0.526
|
84.0
|
1
|
2
|
1.523
|
103
|
527
|
605
|
2.64
|
|
|
|
|
| 技术要求 |
气泡、条纹、应力类级别 |
|
牌 号
|
厚 度(mm)
|
λtj
(nm)
|
λ0
(nm)
|
Tλ0
(%)
|
K
|
|
JB470
|
2
|
470±10
|
560
|
≥89.5
|
≥0.8
|
|
JB490
|
2
|
490±10
|
580
|
≥89.5
|
≥1.2
|
|
JB510
|
2
|
510±10
|
600
|
≥89.5
|
≥1.2
|
|
|
牌 号
|
气 泡
|
条 纹
|
应 力
|
|
JB470
|
C-B
|
3C
|
3
|
|
JB490
|
C-B
|
3C
|
3
|
|
JB510
|
C-B
|
3C
|
3
|
|
|
|
|
|
|
|
|
.........................................................................................................................................................................................................................................................